适用于焊接类似和匹配钢材且含有18% Cr并采用0.5% Ti稳定化的铁素体不锈钢实芯焊丝。该合金通常用于非合金钢和低合金钢的熔敷。 OK Autrod 430Ti还在汽车行业的歧管、催化转换器和排气管焊接上得到广泛应用。Typical Tensile Properties
| Stress relieved |
| Elongation | Stress Relieved Temperature | Stress Relieved Testing Time | Tensile Strength | Yield Strength |
| 24 % | 780 ?C | 0.5 hr | 600 MPa | 390 MPa |
| 28 % | 780 ?C | 0.5 hr | 580 MPa | 380 MPa |
焊缝金属分析
| Mn |
| Mn | Mo | Cu | C | Ti | Si | Ni | Cr |
| 0.5 % | - | - | - | - | - | - | - |
| Mo |
| Mn | Mo | Cu | C | Ti | Si | Ni | Cr |
| - | 0.05 % | - | - | - | - | - | - |
| Cu |
| Mn | Mo | Cu | C | Ti | Si | Ni | Cr |
| - | - | 0.10 % | - | - | - | - | - |
| C |
| Mn | Mo | Cu | C | Ti | Si | Ni | Cr |
| - | - | - | 0.07 % | - | - | - | - |
| Ti |
| Mn | Mo | Cu | C | Ti | Si | Ni | Cr |
| - | - | - | - | 0.400 % | - | - | - |
| Si |
| Mn | Mo | Cu | C | Ti | Si | Ni | Cr |
| - | - | - | - | - | 0.9 % | - | - |
| Ni |
| Mn | Mo | Cu | C | Ti | Si | Ni | Cr |
| - | - | - | - | - | - | 0.3 % | - |
| Cr |
| Mn | Mo | Cu | C | Ti | Si | Ni | Cr |
| - | - | - | - | - | - | - | 17.6 % |
熔敷数据
| 直径 | 安培 | 熔敷率 | 电压 V | 送丝速度 |
| 0.9 mm | - | - | - | - |
| 1.0 mm | 80-190 A | 1,1-3,1 kg/h | 16-24 V | 2,9-8,4 m/min |
| 1.2 mm | 180-280 A | 2,6-4,5 kg/h | 20-28 V | 4,9-8,5 m/min |
| 1.6 mm | 230-350 A | 3-5,2 kg/h | 24-28 V | 3,2-5,5 m/min |