OK 63.30伊萨焊材

适用于18Cr 12Ni 2.8Mo牌号不锈钢焊接的超低碳含量不锈钢焊条。其也适用于焊接成分类似的稳定化不锈钢，母材需要满足足够抗蠕变性时除外。
Typical Tensile Properties
As welded
Elongation
Tensile Strength
Yield Strength
保护气体
40 %
570 MPa
460 MPa
ISO
-
-
-
AWS

夏比V型缺口冲击性能
As welded
Impact Value
Testing Temperature
保护气体
60 J
20 ?C
ISO
55 J
-20 ?C
ISO
43 J
-60 ?C
ISO

焊缝金属分析
Mn
Mn
Mo
C
Si
Ferrite FN
Ni
N
Cr
0.6 %
-
-
-
-
-
-
-
Mo
Mn
Mo
C
Si
Ferrite FN
Ni
N
Cr
-
2.6 %
-
-
-
-
-
-
C
Mn
Mo
C
Si
Ferrite FN
Ni
N
Cr
-
-
0.02 %
-
-
-
-
-
Si
Mn
Mo
C
Si
Ferrite FN
Ni
N
Cr
-
-
-
0.8 %
-
-
-
-
Ferrite FN
Mn
Mo
C
Si
Ferrite FN
Ni
N
Cr
-
-
-
-
6 %
-
-
-
Ni
Mn
Mo
C
Si
Ferrite FN
Ni
N
Cr
-
-
-
-
-
11.0 %
-
-
Cr
Mn
Mo
C
Si
Ferrite FN
Ni
N
Cr
-
-
-
-
-
-
-
18.1 %

熔敷数据
Fusion time per electrode at 90% I max
kg weld metal/kg electrodes
Number of electrodes/kg weld metal
安培
熔敷率
电压 V
直径
37 sec
0.56 kg
250
30-45 A
0.4 kg/h
29 V
1.6 x 300 mm
39 sec
0.60 kg
147
45-65 A
0.6 kg/h
29 V
2.0 x 300 mm
45 sec
0.55 kg
96
45-90 A
0.9 kg/h
29 V
2.5 x 300 mm
57 sec
0.55 kg
52
60-125 A
1.4 kg/h
30 V
3.2 x 350 mm
57 sec
0.56 kg
34
70-190 A
2.0 kg/h
32 V
4.0 x 350 mm
63 sec
0.56 kg
21
100-280 A
3.0 kg/h
32 V
5.0 x 350 mm