OK AUTROD 12.64

OK Autrod 12.64是一种适用于非合金钢GMAW焊接的镀铜锰硅合金化G4Si1/ER70S-6实芯焊丝，可用于普通建筑、汽车零件、压力容器制造及造船行业。该焊丝的锰和硅含量比OK Autrod 12.50略高，因而可提高焊缝金属的强度。该特点也可改善其不易受到表面杂质影响的特性，获得平滑美观的焊缝。 该焊丝可配合Ar/CO2混合气体和纯CO2保护气体使用。
Typical Tensile Properties
As welded
保护气体
Elongation
Tensile Strength
Yield Strength
Stress Relieved Temperature
Stress Relieved Testing Time
AWS CO2 (C1)
-
-
-
-
-
EN 80Ar/20CO2(M21)
26 %
595 MPa
535 MPa
-
-
EN CO2 (C1)
25 %
537 MPa
427 MPa
-
-
Stress relieved
保护气体
Elongation
Tensile Strength
Yield Strength
Stress Relieved Temperature
Stress Relieved Testing Time
EN 80Ar/20CO2(M21)
28 %
520 MPa
395 MPa
620 ?C
15 hr

夏比V型缺口冲击性能
As welded
Testing Temperature
保护气体
Impact Value
Stress Relieved Testing Temp
Stress Relieved Testing Time
-29 ?C
AWS CO2 (C1)
-
-
-
20 ?C
EN 80Ar/20CO2(M21)
130 J
-
-
-20 ?C
EN 80Ar/20CO2(M21)
90 J
-
-
-30 ?C
EN 80Ar/20CO2(M21)
75 J
-
-
-40 ?C
EN 80Ar/20CO2(M21)
70 J
-
-
20 ?C
EN CO2 (C1)
110 J
-
-
-29 ?C
EN CO2 (C1)
76 J
-
-
Stress relieved
Testing Temperature
保护气体
Impact Value
Stress Relieved Testing Temp
Stress Relieved Testing Time
20 ?C
EN 80Ar/20CO2(M21)
120 J
620 ?C
15 hr
-20 ?C
EN 80Ar/20CO2(M21)
90 J
620 ?C
15 hr

焊缝金属分析
Mn
Mn
C
Si
1.68 %
-
-
C
Mn
C
Si
-
0.074 %
-
Si
Mn
C
Si
-
-
0.95 %

熔敷数据
安培
熔敷率
电压 V
直径
送丝速度
60-185 A
0,8-2,5 kg/h
18-24 V
0.8 mm
3,2-10 m/min
70-250 A
0,8-3,3 kg/h
18-26 V
0.9 mm
3-12 m/min
80-300 A
1-5,5 kg/h
18-32 V
1.0 mm
2,7-15 m/min
120-380 A
1,2-8 kg/h
18-35 V
1.2 mm
2,3-15 m/min
150-420 A
1,7-8,5 kg/h
22-36 V
1.4 mm
2,5-12 m/min
225-550 A
2,1-11,4 kg/h
28-38 V
1.6 mm
2,3-12 m/min
300-650 A
3,2-12,5 kg/h
32-44 V
2.0 mm
4-15 m/min